UTP A 73 G 2

Hersteller
UTP
Ceweld product
Type
Solid GTAW wire for hardfacing and rebuilding wornout parts.
classification
AWS
A 5.21: ERFeCr-A
EN ISO
14700: S Fe8
W.Nr.
1.4718
DIN
8555: TIG-6-GZ-60-GP
Anwendungen
Rebuilding and hardfacing parts that are subject to abrasion combined with heavy impact.
Type
Solid GTAW wire for hardfacing and rebuilding wornout parts.
Anwendungen
Rebuilding and hardfacing parts that are subject to abrasion combined with heavy impact.
Eigenschaften

CEWELD® MA 600 Tig offers outstanding abrasion resistance combined with heavy shocks, despite the high hardness several layers can be applied without any risk of braking out or chipping of. In case of sensitive base material preheating is recommended at 300 - 400 °C. Old Hardfacing layers should be removed, clean or grind properly before welding.

Classification
AWS
A 5.21: ERFeCr-A
EN ISO
14700: S Fe8
F-nr
71
W.Nr.
1.4718
DIN
8555: TIG-6-GZ-60-GP
Geeignet für

Gear parts, recycling wear blocks, cutters, molds, pumps, stone crushers, knives, scissors, mixers etc.

Schweißpositionen
PA
PB
PC
PD
PE
PF
PG
Rücktrocknung
Not required
Gas acc. EN ISO 14175
I1
Analyse
C Mn Cr Ni Mo Nb V Fe W Co Cu Al Si Ti B N
0.4 0.5 10 0.02 0.005 0.02 Rem. 0.005 3
Mechanische Gütewerte
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 58 HRc
Product sheet
MSDS
product sheet
Ask quotation
MSDS
Type
1.4718 Solid 600 HB GMAW welding wire for Mig/Mag hardfacing and rebuilding wornout parts.
classification
AWS
A 5.21: ERFeCr-A
EN ISO
14700: S Fe8
W.Nr.
1.4718
DIN
8555: MSG-6-GZ-60-GP
Anwendungen
Rebuilding and Hardfacing parts that are subject to abrasion combined with heavy impact.
Type
1.4718 Solid 600 HB GMAW welding wire for Mig/Mag hardfacing and rebuilding wornout parts.
Anwendungen
Rebuilding and Hardfacing parts that are subject to abrasion combined with heavy impact.
Eigenschaften

CEWELD® MA 600 offers outstanding abrasion resistance combined with heavy shocks, despite the high hardness several layers can be applied without any risk of braking out or chipping of. In case of sensitive base material preheating is recommended at 300-400°C. Old Hardfacing layers should be removed, clean or grind properly before welding.

Classification
AWS
A 5.21: ERFeCr-A
EN ISO
14700: S Fe8
F-nr
71
W.Nr.
1.4718
DIN
8555: MSG-6-GZ-60-GP
Geeignet für

Car recycling, cutters, pumps, stone crushers, knives, scissors, mixers etc.

Schweißpositionen
PA
PB
PC
PD
PE
PF
PG
Rücktrocknung
Not required
Gas acc. EN ISO 14175
M21
Analyse
C Mn Cr Ni Mo Nb V Fe W Co Cu Al Si Ti B N
0.4 0.5 10 0.02 0.005 0.02 Rem. 0.005 3
Mechanische Gütewerte
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 60 HRc
Product sheet
MSDS
product sheet
Ask quotation
MSDS
Type
Solid welding wire for hardfacing and rebuilding wornout parts.
classification
AWS
A 5.21: ERFe-8
EN ISO
14700: S Fe8
W.Nr.
1.2606
DIN
8555: MSG 3-GZ-60-T
Anwendungen
Rebuilding or cladding wornout parts that needs to sustain high abrasion and medium impact.
Type
Solid welding wire for hardfacing and rebuilding wornout parts.
Anwendungen
Rebuilding or cladding wornout parts that needs to sustain high abrasion and medium impact.
Eigenschaften

Solid welding wire for Hardfacing parts that are subject to high abrasion, the addition of tungsten, vanadium and molybdenum offers better cutting properties and higher hardness. Hardness: 570-660 HB

Classification
AWS
A 5.21: ERFe-8
EN ISO
14700: S Fe8
F-nr
71
W.Nr.
1.2606
DIN
8555: MSG 3-GZ-60-T
Geeignet für

Mixer blades, cutting knives, pumps, loader teeth, screws, sludge disposal, carbidge recycling etc.

Schweißpositionen
PA
PB
PC
PF
Rücktrocknung
Not required
Gas acc. EN ISO 14175
M21
Analyse
C Mn Cr Ni Mo Nb V Fe W Co Cu Al Si Ti B N
0.4 0.5 5 1.4 0.3 Rem. 1.3
Mechanische Gütewerte
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 60 HRc