CEWELD® AA MCrMo1V is a metal cored wire wire with Excellent weld puddle manipulation. Low spatter loss, without slag. Extremely crack resistant. Suitable for economic welding of CrMoV-steels up to 550 °C. Due to the seamless production process the hydrogen content is below 3ml/100g weld metal even after long storage in unconditioned conditiond. Good gap bridging properties. In the current range (PF) of 85 - 175 A for vertical up seams suitable.
Typ 1Cr0,5Mo,V ISO 15608: ~5,1
1.7335, 1.7262, 1.7728, 1.7218, 1.7225, 1.7258, 1.7354, 1.7357, 1.7745, 1.7706, 1.7733
13CrMo4-5, 15CrMo5, 15 CrMoV 5 10, 16CrMoV4, 25CrMo4, 42CrMo4, 24CrMo5, G22CrMo5-4, G17CrMo5-5, 24CrMoV5-5, G17CrMoV5-10
ASTM A 182 Gr. F12; A 193 Gr. B7; A 213 Gr. T12; A 217 Gr. WC6; A 234 Gr. WP11; A335 Gr. P11, P12; A 336 Gr. F11, F12; A 426 Gr. CP12
Quenched and tempered ( 30 min at 950º C / oil and 16 h at 700ºC furnace cooling to 300º C )
Rp0,2 >440 MPa Rm 590-780 MPa A5 > 15
Quenched and tempered ( 30 min at 950º C / air and 16 h at 700ºC furnace cooling to 300º C )
Rp0,2 >440 MPa Rm 590-780 MPa A5 > 15
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Impact Energy (J) ISO-V | Hardness |
|---|---|---|---|---|---|
| RT | |||||
| 690°C±15°C 6h | 550 | 700 | 20 | 70 | HRc |