Type
C, Cr, V-, W alloyed cored wire for hardfacing applications. (1.2564)
classification
EN ISO
14700: T Fe3
W.Nr.
1.2567
DIN
MSG 3–GF-45-T
Applications

Rebuilding wornout parts that faces wear and impact combined with increased working temperatures. Hot dies, dies, punches, hammer dies, drawing rings Forging dies, mandrels slab shears, hot cuts, etc.

Type
C, Cr, V-, W alloyed cored wire for hardfacing applications. (1.2564)
Applications

Rebuilding wornout parts that faces wear and impact combined with increased working temperatures. Hot dies, dies, punches, hammer dies, drawing rings Forging dies, mandrels slab shears, hot cuts, etc.

Properties

Machinable ,Heat resistant weld deposit with excelent wear resistance. The weld deposit can be heat treated to offer maximum service protection.  Tempered 560° C ~ 52 HRc Tempered 450° C ~ 49 HRc Tempered 350° C ~ 48 HRc Soft annealed 250 HB

Classification
EN ISO
14700: T Fe3
W.Nr.
1.2567
DIN
MSG 3–GF-45-T
Suitable for

45-52 HRc 

1.2567, 1.2365, 1.2713, 1.2714, 1.2581

30WCrV17 2, 32CrMoV12-283, 55NiCrMoV6, 55NiCrMoV7,  X30WCrV9-3 

Welding positions
PA
PB
Redrying
140°C / 2 hr
Hardening : 1060° C-1120° C°, hot bath, compressed air.
Tempering : approx. 3 h / temperature depending on desired working hardness.
Soft annealing : 2 - 4 h at 800° C -840° C / furnace cooling
Gas acc. EN ISO 14175
M13
Analysis
C Si Mn Cr V W Fe
0.3 0.75 0.8 2.5 0.6 4.5 Rem.
Mechanical Properties
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 47 HRc
580°C±15°C 1h 53 HRc